Effects of morphology and composition on catalytic performance of double metal cyanide complex catalyst

Double metal cyanide (DMC) complexes based on Zn₃[Co(CN)₆]₂ were prepared using different zinc salts and complexing agents and They were characterized by elemental analysis, IR and XRD. The catalytic properties of DMC complexes were determined in polymerization of propylene oxide. Great differences in morphology of DMC complexes was were correlated with preparation route as well as with the kind of zinc salts employed. The catalytic activity was strongly dependent on the morphology of DMC complexes and composition of catalysts. The study revealed that the amorphous catalyst made from ZnCl₂ and t-BuOH had the highest activity (up to 26 kg polymer/g catalyst). The DMC catalyst was non-stoichiometric. Polymerization of propylene oxide (PO) catalyzed by DMC proceeded in a controlled manner. The molecular weight of each polymer was controlled by the monomer/initiator ratio, the values of molecular weight distribution (MWD) were in the range of 1.23–1.48. The polymer has an atactic structure and a head-to-tail regiosequance.     

杯芳烃基嵌段聚醚的合成及界面性质

以对叔丁基苯酚杯[4]芳烃、杯[6]芳烃、杯[8]芳烃、线型酚醛树脂作起始剂，分别与环氧丙烷、环氧乙烷加成，合成了3个系列杯芳烃聚醚类和1个系列线型聚醚类非离子表面活性剂，研究了它们在3种沥青质模型油／去离子水体系的界面活性，考察了其结构与界面活性的关系。在3种沥青质模型油／水体系中，各类聚醚都能替换一部分沥青质而吸附在界面上，有效地降低了油-水界面张力，并在一定浓度时达到饱和吸附，表现出各自的特点和规律。杯芳烃聚醚较线型聚醚的界面活性高，更易吸附在油一水界面，其中又以杯[8]芳烃聚醚的界面活性最高，降低界面张力的能力最强。     

MDI聚氨酯/聚硅氧烷IPN的结构与力学性能

用MDI聚醚氨酯和含少量苯基的聚二甲基硅氧烷合成了一系列的聚氨酯／聚硅氧烷IPN阻尼弹性体，研究了材料的结构与力学性能．结果表明，当聚氨酯与聚硅氧烷的质量比为90：10时。IPN的抗张强度达41．57MPa，断裂伸长率为376％，并具有良好的阻尼性能，玻璃化转变温度范围大于80℃．聚氨酯／聚硅氧烷IPN具有细微的微相分离结构，聚硅氧烷在IPN中的微相尺寸为微米级，并趋向于分布在IPN的表面．     

钻井液降滤失剂聚合醇PEA的研制与评价

合成出了一种用作钻井液降滤失剂的新聚合醇类产品——PEA。介绍了丙三醇与环氧氯丙烷的聚合产物PEA的最佳合成条件：ECH与丙三醇的物质的量比为1．0：1．0；碱与ECH的物质的量比为1．2：1．0；溶剂为丙酮，催化剂为氯化铝。评价了聚合醇PEA在淡水浆、4％盐水浆和MMH正电胶井浆中的降滤失效果。实验结果表明，聚合醇PEA可以用作水基钻井液的降滤失剂，而且PEA在4％盐水浆中的降滤失效果好于其在淡水浆中的降滤失效果，加量大于40．0g／L时，在淡水浆中降滤失率大于84％，表观粘度有所增加，滤饼质量得到改善，在4％盐水浆中降滤失率大于89．1％，表观粘度有一定增加，但增加幅度小于淡水浆；在淡水浆中，PEA在高温高压下仍有良好的降滤失效果，可以抗120℃的高温；PEA可用于正电胶钻井液，并与其它多种处理剂配伍性较好。     

用于稠油脱水的油水两亲破乳剂BC-068的研制与应用

研制了新疆克拉玛依九区稠油专用的破乳剂BC-068。所用起始剂为含多活泼基团的星形聚合物，合成的嵌段聚醚中起始剂与亲油头之比在1：100～268范围，EO含量为25％～55％，经一种油水两亲的两性化合物改性(扩链)，得到高分子量、油水两亲的改性聚醚破乳剂。在75℃、加剂量为100mg／L时，BC-068对九区92号站含水48．6％的稠油脱水率高达99％，脱出水清，油水界面齐，其脱水性能优于所有对比药剂，包括92号站现用药剂PR-02。加剂量降至80、60mg/L或温度降至70℃、65℃时，BC-068的脱水性能均优于PR-02，特别是在较低温度下。在92号站进行为期38天的现场试验，BC-068替换PR-02，加剂量由105mg／L逐步降至81mg／L，净化油含水由11．2％降至0．77％，污水含油由3657mg/L降至2645mg／L。此后BC-068在92号站投入使用，使原来的原油热-电-化学脱水工艺简化为热化学脱水工艺。图1表4。     

中低相对分子质量多元醇类钻井液添加剂PA的研究与应用

通过中低相对分子质量多元醇对钻井液性能影响的试验，找出一种多元醇做主剂，选择其他几种多元醇与其进行复配，弥补单剂多元醇的缺点。采用正交试验，筛选出多元醇类钻井液添加剂PA的最佳配方。结果表明，添加剂PA与聚合物钻井液配伍性好，不影响聚合物钻井液的流变性，提高钻井液的润滑性和膨胀抑制性。多元醇类钻井液添加剂PA已在塔里木油田柯深101井成功应用，取得较好效果。     

多功能聚醚多元醇防塌剂SYP-1的性能评价及现场应用

新型多功能钻井液用防塌剂SYP-1是以低分子量醇为起始剂,由环氧乙烷(简称EO)和环氧丙烷(简称PO)共聚而成的聚醚型多元醇防塌剂,为白色或淡黄色粘稠液.室内试验对聚醚多元醇防塌剂SYP-1的性能进行了评价,结果表明,聚醚多元醇防塌剂SYP-1具有很强的抑制作用和良好的润滑性能,能显著降低钻井液摩擦系数,提高极压膜强度,对钻井液流变性影响小,能改善钻井液滤失性能,基本不发泡,保护油气层能力强;且无毒、易生物降解,满足环境保护要求;荧光级别小于3级,是一种适用于深井、定向井和水平井的高性能防塌剂.分析了多功能聚醚多元醇防塌剂SYP-1的作用机理,介绍了其现场应用情况.该防塌剂已在胜利油田、塔里木油田及吐哈油田推广应用,很好地解决了井壁坍塌和钻井液润滑性问题.     

Characterisation of polyurethane networks based on vegetable derived polyol

A polyurethane (PU) network based on vegetable derived polyol has been characterised and compared to a synthetic based network. Fracture mechanics studies showed the lowest tear strength for the vegetable networks, which decreased as molecular weight of the vegetable based polyol increased. Swelling studies were carried out to determine the molecular weight between crosslinks and polymer networks made from wholly synthetic polyols were shown to have higher molecular weight between crosslinks. Moreover, vegetable networks showed higher solubles' content. Sol-fractions were analysed by several techniques. It was found that vegetable networks based sol-fraction was mainly its correspondent raw polyol while low molecular weight oligomers were detected for the most part in synthetic networks based sol-fraction.     

竹粉在多元醇中热化学液化的研究

以不同多元醇作为液化剂,硫酸为催化剂,在液固比为10∶3的条件下将竹粉一次性加入进行液化,研究了竹粉的液化效率,采用了分步液化法来降低液固比.结果表明,竹粉一次性加入进行液化,聚乙二醇(PEG-400)/甘油(质量比80/20)混和液化剂的液化效果最好;分步液化时在液固比为10∶6的情况下,PEG/甘油体系中的液化残渣率可控制在10%以内,同时液化产物还具有良好的流动性,羟值为230～310 mgKOH/g,适用于聚氨酯胶粘剂的制备.     

一种新型聚醚多元醇的合成及其诱导期研究

用自制的双金属氰化物络合物催化剂(DMC)合成了以酚醛树脂为起始剂的聚醚多元醇。并利用温度与时间曲线分析合成反应的诱导期,考察了起始温度、催化剂浓度、起始剂用量以及单体浓度等对诱导期及最大反应压力的影响,并表征了酚醛聚醚多元醇的结构。结果表明,酚醛树脂中羟基浓度0.0037 mol.L-1、环氧丙烷18 mL(占物料总质量的95%)、催化剂DMC质量分数470×10-6%及温度110℃左右为最佳反应条件。